Rotor rod Dia 50mm Head szie 140-150mm graphite rotor and shaft for degassing in aluminium industry/graphite Обустройство дома - купить
Специальная цена *
Категория товара: Крепления
История изменения цены
Купить Rotor rod Dia 50mm Head szie 140-150mm graphite rotor and shaft for degassing in aluminium industry/graphite | Обустройство дома
Hi-Tech Carbon Co.,Limited
Graphite Rotor
Size
| No. |
Rotor rod szie(mm) |
Rotor Head szie(mm) |
Total Length (mm) |
Price per set |
Weight kg |
|
| Common treatment |
Special treatment Anti Erode of additive |
|
||||
| 001 |
Dia 50 |
Dia 140-150 |
750-800 |
USD190 |
USD380 |
5 |
| 002 |
Dia70-80 |
Dia 180-200 |
900-1100 |
USD290 |
USD580 |
15 |
| 003 |
Dia 150 |
Dia 220-250 |
850-950 |
USD680 |
USD810 |
14 |
| 004 |
Dia 150 |
Dia 350 |
1750-1800 |
USD1050 |
USD1550 |
63.5 |
Raw material of the graphite rod/shaft
| Index |
graphite head / impeller |
graphite rod/shaft |
| Die mold graphite |
Extruded Graphite GSK 0.8 |
|
| Bulk density |
1.85 g/cm3 |
≥1.75 g/cm3 |
| Particle |
≤43 um |
≤ 0.8 MM (800um) |
| Electric resistivity |
≥9 unm |
≥8 unm |
| Bending strength |
≥45 Mpa |
≥17 Mpa |
| resist compression |
≥65 Mpa |
≥32 Mpa |
| Ash |
≤0.1 % |
≤0.1 % |
Applications
In the aluminum and zinc casting industries, nitrogen, argon or carbon tetrachloride are injected and sprayed into molten metal through graphite rotors for dehydrogenation.
It can eliminate the bubbles inside the castings and improve their inner quality. Injects inert gases into the Metallic solution
Property/ Supper strong bending strength and supper high Compressive strength;Strong oxidation resistance
Service Life/ About 700 C, 55-65 days More than 1000 C, 25-35 days (depending on the size and operation)